Features:

• Less Odor / Excellent Quality – PolyLite™ ABS is made with a specialty bulk-polymerized ABS resin, which has significantly lower volatile content compared to traditional ABS resins. It delivers excellent printing quality with minimal odor during printing.
• Balanced Mechanical / Thermal Properties – PolyLite™ ABS features well balanced mechanical and thermal properties, outperforming regular PLA and PETG in toughness and featuring a heat resistance up to 100°C.
• Affordable Technology – Polymakers industry leading filament quality and technology now available at an affordable price
• Uncompromised Quality – With Polymaker’s industry leading quality control process and rigorous in-house testing, you can rest assured that PolyLite™ ABS will produce beautiful, reliable and accurate printed parts.

Specifications:

Print Settings

• Nozzle Temperature: 245˚C – 265˚C
• Printing Speed: 30mm/s – 50mm/s
• Bed Temperature: 90˚C – 100˚C
• Bed Surface: BuildTak®, PEI sheet with ABS slurry
• Cooling Fan: OFF

Other: When printing with PolyLite™ ABS it is recommended to use an enclosure. For large part it is recommended to use a heated chamber.

Note: Printing conditions may vary with different printers and nozzle diameters

Mechanical Properties (X-Y)

• Young’s Modulus: 2174 ± 285 Mpa
• Tensile Strength: 33.3 ± 0.8 Mpa
• Bending Strength: 72.8 ± 0.7 Mpa
• Impact Strength: 12.6 ± 1.1 kJ/m2

Thermal Properties

• Glass Transition Temperature: 101.1˚C
• Heat Deflection Temperature (0.45 MPa): 99.6˚C
• Heat Deflection Temperature (1.8 MPa): 98.2˚C
• Vicat Softening Temperature: 103.9˚C

Notes

• Density: 1.12 g/cm3
• See Safety Data Sheets

Disclaimer: The typical values presented in Polymakers data sheet are intended for reference and comparison purposes only. Due to the nature of 3D printing they should not be used for design specifications or quality control purposes.

Storage: It is recommended to store PolyLite™ ABS in the PolyBox™ to prevent moisture absorption which will lower the quality and the mechanical properties of the print. If the filament has absorbed moisture it can be dried at 70˚C for 6 hours in a convection oven.